PROPERTIES
STANDARD
CONDITION
UNIT
PA6
glass fiber reinforced glassfiber &
Mineral reinforced
AG20TKB
(BK)
AG30TKB
(BK)
AG35TKB
(BK)
AMG40TKB
(BK)
PHYSICAL         
Density ISO 1183 23℃ g/㎤ 1.26 1.36 1.41 1.48
Ash Content ISO 3451/1 950℃ % 20±2 30±3 35±3 40±3
Moisture Content ISO 15512 - % 0.04 0.04 0.04 0.04
Mould Shrinkage SHINIL - % 0.3~0.6 0.3~0.6 0.3~0.6 0.4~0.6
MECHANICAL        
Tensile Modulus ISO 527 5mm/min MPa 7000 9800 10900 9200
Tensile Stress at Break ISO 527 5mm/min MPa 141 183 190 120
Flexural Modulus ISO 178 2mm/min MPa 6750 8650 9700 8500
IMPACT       
Notched Izod Impact Strength ISO 180/1A 23℃ KJ/㎡ 4.0 15.0 15.0 5.0
ISO 180/1A -40℃ KJ/㎡ 3.0 11.0 12.0 4.0
Notched Charpy Impact Strength ISO 179/1eA 23℃ KJ/㎡ 4.0 14.0 15.0 5.0
ISO 179/1eA -30℃ KJ/㎡ 3.0 12.0 13.0 4.0
THERMAL        
HDT ISO 75-1/2 1.80MPa 210 210 210 200
Melting Temperature ISO 3146 10℃/min 220 220 220 220
BURNING BEHAIOR     
Flame Retardant UL94 - CLASS HB HB HB HB
ELECTRICAL       
Surface Resistivity ICE 60093 23℃/50% R.H Ω.m E^14 E^14 E^14 E^14
PROCESSING IMFORMATION        
Predrying - 2~4Hr 60 60 60 60
Processing Temp. - - 240~270 240~270 240~270 240~270
APPLICATION
APPLICATION       brackets air intake maniford cylinder head cover inside door handle
SHINIL CHEMICAL INDUSTRY CO., LTD      


PROPERTIES
STANDARD
CONDITION
UNIT
PA 66
glass fiber reinforced glassfiber &
Mineral reinforced
WG20TKB
(BK)
AG30TKB
(BK)
AG35TKB
(BK)
AMG40TKB
(BK)
PHYSICAL        
Density ISO 1183 23℃ g/㎤ 1.26 1.36 1.41 1.48
Ash Content ISO 3451/1 950℃ % 20±2 30±3 35±3 40±3
Moisture Content ISO 15512 - % 0.04 0.04 0.04 0.04
Mould Shrinkage SHINIL - % 0.3~0.6 0.3~0.6 0.3~0.6 0.4~0.6
MECHANICAL       
Tensile Modulus ISO 527 5mm/min MPa 7000 9800 10900 9200
Tensile Stress at Break ISO 527 5mm/min MPa 141 183 190 120
Flexural Modulus ISO 178 2mm/min MPa 6750 8650 9700 8500
IMPACT        
Notched Izod Impact Strength ISO 180/1A 23℃ KJ/㎡ 4.0 15.0 15.0 5.0
ISO 180/1A -40℃ KJ/㎡ 3.0 11.0 12.0 4.0
Notched Charpy Impact Strength ISO 179/1eA 23℃ KJ/㎡ 4.0 14.0 15.0 5.0
ISO 179/1eA -30℃ KJ/㎡ 3.0 12.0 13.0 4.0
THERMAL        
HDT ISO 75-1/2 1.80MPa 210 210 210 200
Melting Temperature ISO 3146 10℃/min 220 220 220 220
BURNING BEHAIOR     
Flame Retardant UL94 - CLASS HB HB HB HB
ELECTRICAL        
Surface Resistivity ICE 60093 23℃/50% R.H Ω.m E^14 E^14 E^14 E^14
PROCESSING IMFORMATION        
Predrying - 2~4Hr 60 60 60 60
Processing Temp. - - 240~270 240~270 240~270 240~270
APPLICATION
APPLICATION       brackets air intake maniford cylinder head cover inside door handle
SHINIL CHEMICAL INDUSTRY CO., LTD      

PROPERTIES
PA66
glass fiber reinforced impact
modified
WG20TKB
(BK)
WG25TKB
(BK)
WG30TKB
(BK)
WG33TKB
(BK)
WG35TKB
(BK)
WG40TKB
(BK)
WST80N
(NP,BK)
PHYSICAL        
Density 1.26 1.32 1.37 1.38 1.41 1.45 1.09
Ash Content 20±3 25±3 30±3 33±3 35±3 40±3 -
Moisture Content 0.04 0.04 0.04 0.04 0.04 0.04 0.04
Mould Shrinkage 0.4~0.8 0.4~0.8 0.3~0.7 0.3~0.7 0.3~0.7 0.3~0.6 1.4~1.7
MECHANICAL        
Tensile Modulus 6500 7300 9600 9800 11000 12500 2100
Tensile Stress at Break 125 145 175 180 200 220 52
Flexural Modulus 5500 6500 8500 8700 100000 11000 1900
IMPACT     
Notched Izod Impact Strength 6.0 6.0 9.0 11.0 12.0 14.0 NB
5.0 5.0 7.0 10.0 12.0 13.0 NB
Notched Charpy Impact Strength 6.0 6.0 8.0 10.0 12.0 - NB
5.0 5.0 7.0 9.0 11.0 - NB
THERMAL        
HDT 245 245 245 245 245 245 65
Melting Temperature 260 260 260 260 260 260 260
BURNING BEHAIOR     
Flame Retardant HB HB HB HB HB HB HB
ELECTRICAL       
Surface Resistivity E^14 E^14 E^14 E^14 E^14 E^14 E^14
PROCESSING IMFORMATION        
Predrying 80 80 80 80 80 80 80
Processing Temp. 270~290 270~290 270~290 270~290 270~290 270~290 270~290
APPLICATION
APPLICATION    brackets water pump housing cylinder head cover gear shift
housing
cylinder
head cover
padal ski binding
parts

PROPERTIES
PA66
glass fiber &
PTFE/MoS2 reinforced
glass fiber &
Mineral reinforced
glass fiber &
High density reinforced
glass fiber reinforced
Flame Retardant
WG35TMS
(BK)
WG30PT
(NP)
WM40PT
(BK)
WGM40TKB
(BK)
WG65BS
TKB
WG30F
(NP,Col)
PHYSICAL        
Density 1.41 1.51 1.61 1.46 2.05 1.67
Ash Content 35±3 45±3 55±3 40±3 65±2 30±2
Moisture Content 0.04 0.04 0.05 0.04 0.04 0.04
Mould Shrinkage 0.4~1.0 0.3~0.5 0.5~0.7 0.4~0.7 0.3~0.6 0.3~0.7
MECHANICAL         
Tensile Modulus 11200 9100 7000 9500 9000 9400
Tensile Stress at Break 200 110 80 150 105 150
Flexural Modulus 9600 8500 6500 8800 8650 9000
IMPACT        
Notched Izod Impact Strength 12.0 5.0 4.0 5.0 5.0 5.0
11.0 4.0 3.0 4.0 4.0 4.0
Notched Charpy Impact Strength 11.0 - - 4.0 4.0 -
10.0 - - 3.0 3.0 -
THERMAL       
HDT 245 245 250 240 240 210
Melting Temperature 260 260 260 260 260 260
BURNING BEHAIOR     
Flame Retardant HB HB HB HB HB V-0
ELECTRICAL        
Surface Resistivity E^14 E^14 E^14 E^14 E^14 E^14
PROCESSING IMFORMATION        
Predrying 80 80 80 80 80 80
Processing Temp. 270~290 270~290 270~290 270~290 270~290 240~270
APPLICATION
APPLICATION    gear part vehicle gear lever link friction
bearing
cylinder
head cover
insulation
wall partr
MCCB box